UNS N08367/AL6-XN Stainless Steel Pipe

Availability:

AL-6XN alloy is identified by the Unified Numbering System (UNS) designation of N08367. It is an austenitic stainless steel alloy with high nickel (24%), chromium (22%), molybdenum (6%), and nitrogen (0.18%) content and is commonly known as superaustenitic stainless steel (alloys such as 254 SMO (UNS S31254) and 904L (UNS N08904) also fall under the superaustenitic designation) while 2205 (UNS S32305/ S31803) and 2507 (UNS S32750) are duplex and super duplex stainless steel, respectively.AL-6XN is widely used because it is a 6% moly superaustenitic alloy providing strong resistance to chlorides found in ketchup, barbecue sauce, sports drinks, buffer solutions, and active pharmaceutical ingredients that commonly cause localized corrosion.

Grade	UNS	AISI/ASTM	ID	W.Nr
AL-6XN	N08367	AL6XN
Chemical Composition:
Grade	%	Ni	Cr	Mo	Cu	N
AL-6XN	Min	23.5	20	6	-	0.18
AL-6XN	Max	25.5	22	7	0.75	0.25
	C	Mn	Si	P	S
	-	-	-	-	-
	0.03	2	1.0	0.04	0.03
Physical Performance:
Heat Treatment	*TS**	*YS**	El
Heat Treatment	Rm N/mm2	RP0.2N/mm2	A5 %
Solution	650	300	35

NB	Size	OD mm	40S mm	5S mm	10S mm	S 10 mm	S 20 mm	S 40 mm	S 60 mm	XS/80S mm	S 80 mm	S 100 mm	S 120 mm	S 140 mm	S 160 mm	XXS mm
	1/8”	10.29			1.24			1.73			2.41
	1/4”	13.72			1.65			2.24			3.02
	3/8”	17.15			1.65			2.31			3.20
15	1/2”	21.34	2.77	1.65	2.11			2.77		3.73	3.73				4.78	7.47
20	3/4”	26.67	2.87	1.65	2.11			2.87		3.91	3.91				5.56	7.82
25	1”	33.40	3.38	1.65	2.77			3.38		4.55	4.55				6.35	9.09
32	1 1/4”	42.16	3.56	1.65	2.77			3.56		4.85	4.85				6.35	9.70
40	1 1/2”	48.26	3.68	1.65	2.77			3.68		5.08	5.08				7.14	10.15
50	2”	60.33	3.91	1.65	2.77			3.91		5.54	5.54				9.74	11.07
65	2 1/2”	73.03	5.16	2.11	3.05			5.16		7.01	7.01				9.53	14.02
80	3”	88.90	5.49	2.11	3.05			5.49		7.62	7.62				11.13	15.24
90	3 1/2”	101.60	5.74	2.11	3.05			5.74		8.08	8.08
100	4”	114.30	6.02	2.11	3.05			6.02		8.56	8.56		11.12		13.49	17.12
125	5”	141.30	6.55	2.77	3.40			6.55		9.53	9.53		12.70		15.88	19.05
150	6”	168.27	7.11	2.77	3.40			7.11		10.97	10.97		14.27		18.26	21.95
200	8”	219.08	8.18	2.77	3.76		6.35	8.18	10.31	12.70	12.70	15.09	19.26	20.62	23.01	22.23
250	10”	273.05	9.27	3.40	4.19		6.35	9.27	12.70	12.70	15.09	19.26	21.44	25.40	28.58	25.40
300	12”	323.85	9.53	3.96	4.57		6.35	10.31	14.27	12.70	17.48	21.44	25.40	28.58	33.32	25.40
350	14”	355.60	9.53	3.96	4.78	6.35	7.92	11.13	15.09	12.70	19.05	23.83	27.79	31.75	35.71
400	16”	406.40	9.53	4.19	4.78	6.35	7.92	12.70	16.66	12.70	21.44	26.19	30.96	36.53	40.49
450	18”	457.20	9.53	4.19	4.78	6.35	7.92	14.27	19.05	12.70	23.83	29.36	34.93	39.67	45.24
500	20”	508.00	9.53	4.78	5.54	6.35	9.53	15.09	20.62	12.70	26.19	32.54	38.10	44.45	50.01
550	22”	558.80	9.53	4.78	5.54	6.35	9.53		22.23	12.70	28.58	34.93	41.28	47.63	53.98
600	24”	609.60	9.53	5.54	6.35	6.35	9.53	17.48	24.61	12.70	30.96	38.89	46.02	52.37	59.54
650	26”	660.40	9.53			7.92	12.70			12.70
700	28”	711.20	9.53			7.92	12.70			12.70
750	30”	762.00	9.53	6.35	7.92	7.92	12.70			12.70
800	32”	812.80	9.53			7.92	12.70	17.48		12.70
850	34”	863.60	9.53			7.92	12.70	17.48		12.70
900	36”	914.40	9.53			7.92	12.70	19.05		12.70

Grades	C max	Mn max	P max	S max	Si max	Cr	Ni	Mo
304	0.08	2.00	0.04	0.03	0.075	18.00-20.00	8.00-11.00	/
304L	0.035	2.00	0.04	0.03	0.075	18.00-20.00	8.00-13.00	/
316	0.08	2.00	0.04	0.03	0.075	16.00-18.00	11.00-14.00	2.00-3.00
316L	0.035	2.00	0.04	0.03	0.075	16.00-18.00	10.00-15.00	2.00-3.00

Grades	Itemper	Tensile Psi	Yield Psi	Elong %	Rockwell Hardness
304	Annealed	85000-105000	35000-75000	20-55	80-95
304L	Annealed I1/8 Hard	80000-105000	30000-75000	20-55	75-95
316	Annealed	85000 min	35000 min	50 min	80 min
	Annealed	80000 min	30000 min	50 min	75 min