Inconel Pipe

Availability:

Inconel 600 Corrosion resistance 600 have corrosion resistance to many kinds of corrosive media. The material produced by Beall Industry group are of high quality.Chromium content made it with better corrosion resistance than Nickel 99.2 (alloy200) and Nickel 99.2 ( alloy201,low carbon) in the oxidize environment. Meantime, high Nickel content make this alloy with good corrosion resistance in the reduction condition and alkaline solution, and also effective avoid chlorine-iron stress corrosion cracking. 600 have good corrosion resistance in the acid, acetic acid, formic acid, stearic acid and other organic acid, with medium corrosion resistance in the inorganic acid. The alloy with excellent corrosion resistance in the first and the second recycling use of the high purity water in the nuclear reactor. Especially excellent corrosion resistance to dry chlorine and chlorine hydride applied up to 650 ℃. When nder the high temperature, annealing and state solution alloy have good antioxidant off and high-intensity in the air, 600 can resist the ammonia, nitriding and carburizing atmosphere, but at the turn of the changes in redox conditions, it will be corrosion by parts of oxidation media.( such as green death liquid)

Grade	Inconel 600 – UNS N06600, Inconel 601 – UNS N06601, Inconel 625 – UNS N06625, Incoloy 800 – UNS N08800, Incoloy 800H / HT – UNS N08810, Incoloy 825 – UNS N08825
Specification	IS, BS, ASTM
Type	Seamless Weled

Alloy	Common Name	Related Specification
		British	European	ASTM	UNS
Alloy 600	Inconel 600 ®	BS 3076 NA 14	2.4816	B166	N06600

Alloy	Common Name	Related Specification
		British	European	ASTM	UNS
Alloy 625	Inconel 625 ®	BS 3076 NA 21	2.4856	B446	N06625

Alloy	Common Name	Related Specification
		British	European	ASTM	UNS
Alloy 718	Inconel 718 ®		1.4668	B637	N07718

Inconel 600	Ni	Fe	C	Mn	Si	Cu	Cr	S
Inconel 600	72.0 min	6.0 – 10.0	0.15 max	1.0 max	0.5 max	0.5 max	14.0 – 17.0	0.015 max

Inconel Pipe

Related Products

Telephone

Email

Products

About Us

Quick Links

Subscribe to our newsletter

Density	8.47 g/cm3
Melting Point	1413 °C (2580 °F)
Tensile Strength	Psi – 95,000 , MPa – 655
Yield Strength (0.2%Offset)	Psi – 45,000 , MPa – 310
Elongation	40 %

Density	8.4 g/cm3
Melting Point	1350 °C (2460 °F)
Tensile Strength	Psi – 1,35,000 , MPa – 930
Yield Strength (0.2%Offset)	Psi – 75,000 , MPa – 517
Elongation	42.5 %

NB	Size	OD mm	40S mm	5S mm	10S mm	S 10 mm	S 20 mm	S 40 mm	S 60 mm	XS/80S mm	S 80 mm	S 100 mm	S 120 mm	S 140 mm	S 160 mm	XXS mm
	1/8”	10.29			1.24			1.73			2.41
	1/4”	13.72			1.65			2.24			3.02
	3/8”	17.15			1.65			2.31			3.20
15	1/2”	21.34	2.77	1.65	2.11			2.77		3.73	3.73				4.78	7.47
20	3/4”	26.67	2.87	1.65	2.11			2.87		3.91	3.91				5.56	7.82
25	1”	33.40	3.38	1.65	2.77			3.38		4.55	4.55				6.35	9.09
32	1 1/4”	42.16	3.56	1.65	2.77			3.56		4.85	4.85				6.35	9.70
40	1 1/2”	48.26	3.68	1.65	2.77			3.68		5.08	5.08				7.14	10.15
50	2”	60.33	3.91	1.65	2.77			3.91		5.54	5.54				9.74	11.07
65	2 1/2”	73.03	5.16	2.11	3.05			5.16		7.01	7.01				9.53	14.02
80	3”	88.90	5.49	2.11	3.05			5.49		7.62	7.62				11.13	15.24
90	3 1/2”	101.60	5.74	2.11	3.05			5.74		8.08	8.08
100	4”	114.30	6.02	2.11	3.05			6.02		8.56	8.56		11.12		13.49	17.12
125	5”	141.30	6.55	2.77	3.40			6.55		9.53	9.53		12.70		15.88	19.05
150	6”	168.27	7.11	2.77	3.40			7.11		10.97	10.97		14.27		18.26	21.95
200	8”	219.08	8.18	2.77	3.76		6.35	8.18	10.31	12.70	12.70	15.09	19.26	20.62	23.01	22.23
250	10”	273.05	9.27	3.40	4.19		6.35	9.27	12.70	12.70	15.09	19.26	21.44	25.40	28.58	25.40
300	12”	323.85	9.53	3.96	4.57		6.35	10.31	14.27	12.70	17.48	21.44	25.40	28.58	33.32	25.40
350	14”	355.60	9.53	3.96	4.78	6.35	7.92	11.13	15.09	12.70	19.05	23.83	27.79	31.75	35.71
400	16”	406.40	9.53	4.19	4.78	6.35	7.92	12.70	16.66	12.70	21.44	26.19	30.96	36.53	40.49
450	18”	457.20	9.53	4.19	4.78	6.35	7.92	14.27	19.05	12.70	23.83	29.36	34.93	39.67	45.24
500	20”	508.00	9.53	4.78	5.54	6.35	9.53	15.09	20.62	12.70	26.19	32.54	38.10	44.45	50.01
550	22”	558.80	9.53	4.78	5.54	6.35	9.53		22.23	12.70	28.58	34.93	41.28	47.63	53.98
600	24”	609.60	9.53	5.54	6.35	6.35	9.53	17.48	24.61	12.70	30.96	38.89	46.02	52.37	59.54
650	26”	660.40	9.53			7.92	12.70			12.70
700	28”	711.20	9.53			7.92	12.70			12.70
750	30”	762.00	9.53	6.35	7.92	7.92	12.70			12.70
800	32”	812.80	9.53			7.92	12.70	17.48		12.70
850	34”	863.60	9.53			7.92	12.70	17.48		12.70
900	36”	914.40	9.53			7.92	12.70	19.05		12.70

Grades	C max	Mn max	P max	S max	Si max	Cr	Ni	Mo
304	0.08	2.00	0.04	0.03	0.075	18.00-20.00	8.00-11.00	/
304L	0.035	2.00	0.04	0.03	0.075	18.00-20.00	8.00-13.00	/
316	0.08	2.00	0.04	0.03	0.075	16.00-18.00	11.00-14.00	2.00-3.00
316L	0.035	2.00	0.04	0.03	0.075	16.00-18.00	10.00-15.00	2.00-3.00

Grades	Itemper	Tensile Psi	Yield Psi	Elong %	Rockwell Hardness
304	Annealed	85000-105000	35000-75000	20-55	80-95
304L	Annealed I1/8 Hard	80000-105000	30000-75000	20-55	75-95
316	Annealed	85000 min	35000 min	50 min	80 min
	Annealed	80000 min	30000 min	50 min	75 min